C10 is a plain carbon steel with a nominal 0.10% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased strength. 
Availability:

PDF Export

facebook sharing button
twitter sharing button
whatsapp sharing button
wechat sharing button
sharethis sharing button
  • DIN C10/AISI 1010

C10 is a plain carbon steel with a nominal 0.10% carbon content. It is a relatively low strength steel, but it may be quenched and tempered for increased strength.

Designation by Standards

Mat. No.DINENAISI
1.0301C10-1010


Chemical Composition (in weight %)

CSiMnCrMoNiVWOthers
0.10max. 0.400.45------


Applications
The low carbon steels, such as C10, are used for applications such as cold headed fasteners and bolts.


Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m.K]: 58.6
Electric resistivity [Ohm mm2/m]: 0.11
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC20-200oC
11.011.8


Soft Annealing
Heat to 850-950
oC, cool slowly. This will produce a hardness of 90-100 HB.


Stress Relieving

Stress relieving to remove machining stresses should be carried out by heating to approx. 540oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.


Forging
Hot forming temperature: 1200-950oC. 


Machinability
Machinability of C10 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AISI 1112 as a reference that is considered 100% machinable (easily machined) the C10 steel has a rating of 55%. 

Corrosion Resistance

This is a plain carbon steel and has no corrosion resistance. It will rust unless protected.


Welding
C10 steel may be welded by all of the standard welding techniques.

Cold Working
C10 is easily cold worked by traditional means. Following severe cold working a stress relief, or full, anneal should be performed.


Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.