Mat.No. 1.2063/DIN 145Cr6
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2063 | 145Cr6 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 1.50 | 0.23 | 0.60 | 1.40 | - | - | - | - | - |
ApplicationsSmall to medium size blanking and punching dies, shear blades, thread cutting tools, reamers, gauges and similar measuring instruments.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 740-760oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 830-860oC followed by oil quenching (interrupt at approx. 150oC). Hardness after quenching is 64 HRC.Tempering Temperature (oC) vs. Hardness (HRC)
| 100oC | 200oC | 300oC | 400oC |
| 63.5 | 62 | 59 | 54 |
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2063 | 145Cr6 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 1.50 | 0.23 | 0.60 | 1.40 | - | - | - | - | - |
ApplicationsSmall to medium size blanking and punching dies, shear blades, thread cutting tools, reamers, gauges and similar measuring instruments.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 740-760oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 830-860oC followed by oil quenching (interrupt at approx. 150oC). Hardness after quenching is 64 HRC.Tempering Temperature (oC) vs. Hardness (HRC)
| 100oC | 200oC | 300oC | 400oC |
| 63.5 | 62 | 59 | 54 |
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.