ASTM A335 P11
Packing
Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.
Inspection and Test
Chemical Composition Inspection, Mechanical Properties Test (Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface treatment
Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
ASTM A335 P11 Chemical Compositions(%)
| Compositions | Data |
| UNS Designa-tion | K11597 |
| Carbon | 0.05-0.60 |
| Manganese | 0.30-0.60 |
| Phosphorus(max.) | 0.025 |
| Sulfur(max.) | 0.025 |
| Silicon | 0.50-1.00 |
| Nickel | … |
| Chromium | 1.00-1.50 |
| Molybdenum | 0.44-0.65 |
| Other Elements | … |
Mechanical properties for ASTM A335 P11
| Properties | Data |
| Tensile strength, min, (MPa) | 415 Mpa |
| Yield strength, min, (MPa) | 205 Mpa |
| Elongation, min, (%), L/T | 30/20 |
Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
A / N+T
N+T / Q+T
N+T
Mechanical Tests Specified
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test.
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test
P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Packing
Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.
Inspection and Test
Chemical Composition Inspection, Mechanical Properties Test (Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface treatment
Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
ASTM A335 P11 Chemical Compositions(%)
| Compositions | Data |
| UNS Designa-tion | K11597 |
| Carbon | 0.05-0.60 |
| Manganese | 0.30-0.60 |
| Phosphorus(max.) | 0.025 |
| Sulfur(max.) | 0.025 |
| Silicon | 0.50-1.00 |
| Nickel | … |
| Chromium | 1.00-1.50 |
| Molybdenum | 0.44-0.65 |
| Other Elements | … |
Mechanical properties for ASTM A335 P11
| Properties | Data |
| Tensile strength, min, (MPa) | 415 Mpa |
| Yield strength, min, (MPa) | 205 Mpa |
| Elongation, min, (%), L/T | 30/20 |
Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
A / N+T
N+T / Q+T
N+T
Mechanical Tests Specified
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test.
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test
P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].