0.288 lb/in3 (7972 kg/m3)
Specific Gravity
7.97
| PDF Export | |
HS 6-5-4/E M4/SKH 54 M4
HS 6-5-4/E M4/SKH 54 M4 High Speed Steel
M4 is an extremely versatile high-speed steel with its extremely high carbon and vanadium contents for exceptional abrasion-resistance. It is well suited for premium cutting tools of all types, particularly those used for machining abrasive alloys, castings and heat-treated materials. The high carbon content enables M4 steel to be hardened in excess of 65HRC. However, the high hardness and high vanadium carbide content make it more difficult to grind after heat treatment compared to M2 and other high-speed steels.
Other Known Names: HS 6-5-4, E M4, SKH 54, Stark.
Physical Properties
Density
0.288 lb/in3 (7972 kg/m3)
Specific Gravity
7.97
30 x 106 psi (207 GPa)
Machinability
35-40% of a 1% carbon steel
M4 High Speed Steel Chemical Composition
| MAXIMUM | TYPICAL | ||||||
|---|---|---|---|---|---|---|---|
| Carbon | Chromium | Tungsten | Molybdenum | Vanadium | Cobalt | Annealed | Tempered |
| C | Cr | W | Mo | V | Co | Hb | HrC |
| 1.3 | 4.25 | 5.85 | 4.75 | 4.1 | - | 255 | 65 |
| ANNEALING | PREHEAT | AUSTENITIZING | QUENCH | TEMPERING |
|---|---|---|---|---|
| Temp | Temp | Temp | Medium | Temp |
| °F | °F | °F | °F | |
| 1550/1600 | 1500/1550 | 2175/2225 | Salt/Oil/Atm | 1025/1050 |
HS 6-5-4/E M4/SKH 54 M4 High Speed Steel
M4 is an extremely versatile high-speed steel with its extremely high carbon and vanadium contents for exceptional abrasion-resistance. It is well suited for premium cutting tools of all types, particularly those used for machining abrasive alloys, castings and heat-treated materials. The high carbon content enables M4 steel to be hardened in excess of 65HRC. However, the high hardness and high vanadium carbide content make it more difficult to grind after heat treatment compared to M2 and other high-speed steels.
Other Known Names: HS 6-5-4, E M4, SKH 54, Stark.
Physical Properties
Density
0.288 lb/in3 (7972 kg/m3)
Specific Gravity
7.97
30 x 106 psi (207 GPa)
Machinability
35-40% of a 1% carbon steel
M4 High Speed Steel Chemical Composition
| MAXIMUM | TYPICAL | ||||||
|---|---|---|---|---|---|---|---|
| Carbon | Chromium | Tungsten | Molybdenum | Vanadium | Cobalt | Annealed | Tempered |
| C | Cr | W | Mo | V | Co | Hb | HrC |
| 1.3 | 4.25 | 5.85 | 4.75 | 4.1 | - | 255 | 65 |
| ANNEALING | PREHEAT | AUSTENITIZING | QUENCH | TEMPERING |
|---|---|---|---|---|
| Temp | Temp | Temp | Medium | Temp |
| °F | °F | °F | °F | |
| 1550/1600 | 1500/1550 | 2175/2225 | Salt/Oil/Atm | 1025/1050 |