Mat.No. 1.2360
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2360 | - | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.47 | 0.80 | 0.40 | 7.50 | 1.37 | - | 1.35 | - | - |
Applications
Severely stressed machine blades for cellulose and paper industry, woodworking milling cutters, flat and circular blades for cutting sheets/plates of thickness 5 to 15 mm.
Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Hardening
Harden from a temperature of 1080-1120oC followed by oil quenching.
Tempering
Tempering temperature: Please see the diagram bellow.
Forging
Hot forming temperature: 1100-900oC.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it becomes available.
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2360 | - | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.47 | 0.80 | 0.40 | 7.50 | 1.37 | - | 1.35 | - | - |
Applications
Severely stressed machine blades for cellulose and paper industry, woodworking milling cutters, flat and circular blades for cutting sheets/plates of thickness 5 to 15 mm.
Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Hardening
Harden from a temperature of 1080-1120oC followed by oil quenching.
Tempering
Tempering temperature: Please see the diagram bellow.
Forging
Hot forming temperature: 1100-900oC.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it becomes available.