Mat.No. 1.2564/DIN X30WCrV41
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2564 | X30WCrV41 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.30 | 0.95 | 0.40 | 1.05 | - | - | 0.18 | 3.75 | - |
Applications
Water cooled dummy blocks for the extrusion of copper and copper alloys, hand casting chills for copper alloys.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 820-840oC, cool slowly in furnace. Holding time 4-6 hours. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by slow cooling. Time is 1-2 hours. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 960-1050oC followed by water or oil quenching. Hardness after quenching is appr. 52 HRC (water quenching), 47 HRC (oil quenching).
Tempering
Tempering temperature: 560-700oC.
Nitriding
Possible. Preheating before use: 200-300 oC, absolutely necessary.
Forging
Hot forming temperature: 1100-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2564 | X30WCrV41 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.30 | 0.95 | 0.40 | 1.05 | - | - | 0.18 | 3.75 | - |
Applications
Water cooled dummy blocks for the extrusion of copper and copper alloys, hand casting chills for copper alloys.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 820-840oC, cool slowly in furnace. Holding time 4-6 hours. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by slow cooling. Time is 1-2 hours. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 960-1050oC followed by water or oil quenching. Hardness after quenching is appr. 52 HRC (water quenching), 47 HRC (oil quenching).
Tempering
Tempering temperature: 560-700oC.
Nitriding
Possible. Preheating before use: 200-300 oC, absolutely necessary.
Forging
Hot forming temperature: 1100-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.