Mat.No. 1.2601/DIN X165CrMoV12

Ledeburitic Cr-steel for high performance cutting tools, toughness better than D3, possibility of nitriding. This alloy possesses a very high compressive strength and is deep hardening. 
Availability:

PDF Export

facebook sharing button
twitter sharing button
whatsapp sharing button
wechat sharing button
sharethis sharing button
  • Mat.No. 1.2601/DIN X165CrMoV12

Ledeburitic Cr-steel for high performance cutting tools, toughness better than D3, possibility of nitriding. This alloy possesses a very high compressive strength and is deep hardening.

Designation by Standards

Mat. No.DINENAISI
1.2601X165CrMoV12X160CrMoV121-


CSiMnCrMoNiVWOthers
1.650.330.3011.500.60-0.300.50-


Applications

Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.

Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.70
Thermal conductivity [W/m.K]: 20.0
Electric resistivity [Ohm mm2/m]: 0.65
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC20-200oC20-300oC20-400oC20-500oC
10.511.011.011.512.0


Soft Annealing

Heat to 800-840oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 255.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Harden from a temperature of 980-1010oC followed by oil, air quenching or warm bath quenching. Hardness after quenching is 63-65 HRC.

Tempering
Tempering temperature: 150-400oC.

Tempering Temperature (oC) vs. Hardness (HRC)

100oC200oC300oC400oC
64626058


Forging
Hot forming temperature: 1050-850oC.


Machinability
The machinability rating of OCR12EX is roughly 20-25% that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.