Mat.No. 1.2375/DIN 83CrMoV9
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2375 | 83CrMoV9 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.88 | 0.30 | 0.38 | 2.15 | 0.28 | - | 0.10 | - | - |
Applications
Wear resisting tools, die casting tools, pressing tools for light and heavy metals. This steel grade can be water cooled.
Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.83
Soft Annealing
Brinell hardness in annealed condition is max. 239.
Normalizing
Normalizing temperature: Please ask.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Please ask.
Tempering
Tempering temperature: Please ask.
Forging
Hot forming temperature: 1150-850oC.
Machinability
No data.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it becomes available.
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2375 | 83CrMoV9 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.88 | 0.30 | 0.38 | 2.15 | 0.28 | - | 0.10 | - | - |
Applications
Wear resisting tools, die casting tools, pressing tools for light and heavy metals. This steel grade can be water cooled.
Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.83
Soft Annealing
Brinell hardness in annealed condition is max. 239.
Normalizing
Normalizing temperature: Please ask.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Please ask.
Tempering
Tempering temperature: Please ask.
Forging
Hot forming temperature: 1150-850oC.
Machinability
No data.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it becomes available.